Influence of Maleic-Anhydride-Polypropylene (MAPP) on Wettability of Polypropylene/Wood Flour/Glass Fiber Hybrid Composites
B. Mohebby1 , P. Fallah-Moghadam1 , A. R. Ghotbifar1 , S. Kazemi-Najafi1
1- Department of Wood and Paper Sciences, Faculty of Natural Resources, Tarbiat Modares University, P.O. Box: 46414-356, Noor, Islamic Republic of Iran.
Abstract:   (5873 Views)
The influence of maleic anhydride-polypropylene (MAPP) (0, 2, 3 and 5%) as a compatibilizer on the wettability of polypropylene/wood flour/glass fiber hybrid composites was studied by using the contact angle determination technique. Sample slats with a cross section of 10×70 mm were made by a twin screw extruder. Specimens were conditioned at room temperature and the angles between the water droplets and surfaces of the hybrid composites were measured. Results revealed that the wettability of the composites was significantly decreased as the MAPP was increased to 3%. However, no significant decreasing effect was observed at MAPP contents above 3%.
Keywords: Contact angle, Polypropylene/Wood flour/Glass fiber hybrid composites, Wettability
Full-Text [PDF 152 kb]   (7234 Downloads)    

Received: 2011/05/9 | Accepted: 2011/05/9 | Published: 2011/05/9
Add your comments about this article : Your username or Email:
CAPTCHA
Rights and permissions
Creative Commons License This work is licensed under a Creative Commons Attribution-NonCommercial 4.0 International License.